Low Cement Castables
Reframon LC is a low cement Castable having high strength at all temperature levels. These Castables are used in locations needing high abrasion resistance.
Ultra Low Cement Castables
Reframon ULCC are ultra-low cement castables which contain even lower level of cement than low cement castables.
Above LC/ULCC Castables offers following advantages:
Low CaO content ensures high refractoriness.
Excellent hot strength and MOR at all temperatures.
Lower apparent porosity after firing offers better corrosion resistance.
High abrasion and spalling resistance.
High volume stability.
BRANDS | Reframon ULCC90 | Reframon ULCC95 |
Chemical Analysis | ||
Al2O3% Min. | 90 | 94 |
Fe2O3% Max. | 1.0 | 0.3 |
SiO2% | 7 | 4.1 |
CaO% | 0.9 | 0.9 |
Physical Properties | ||
Service Temp. ˚C | 1750 | 1800 |
Bulk Density gms/cc | 3.00 | 3.00 |
Water required for casting | 4.2 - 5.0 | 4 - 4.8 |
Grain Size, mm | 6.00 | 6.00 |
CCS Kgs/cm2 | ||
At 110 ˚C/24 hrs. | 450 | 400 |
At 800 ˚C/3 hrs. | 1000 | 700 |
At 1100 ˚C/3 hrs. | 1100 | 1000 |
At 1550 ˚C/3 hrs. | 1200 | 1250 |
Thermal Properties | ||
PLC% after | ||
Heating at 800˚C/3 hrs. | + 0.2 | + 0.2 |
Heating at 1100˚C/3 hrs. | + 0.3 | + 0.3 |
Heating at 1450˚C/3 hrs. | ||
Thermal Conductivity Kcal/m/hr/˚C at 400˚C HF | 2.21 | 2.28 |
At 600 ˚C HF | 2.33 | 2.33 |
At 800 ˚C HF | 2.40 | 2.40 |
BRANDS | Reframon LC45 | Reframon LC60 | Reframon LC70 | Reframon LC80 | Reframon LC90 | Reframon LC95 |
Chemical Analysis | ||||||
Al2O3 % Min. | 45 | 60 | 70 | 80 | 90 | 94 |
Fe2O3 % Max. | 1.0 | 1.5 | 1.5 | 1.8 | 1.0 | 0.3 |
SiO% Max. | 50 | 36 | 25 | 14 | 5.7 | 0.22 |
CaO % | 1.7 | 1.7 | 1.3 | 1.8 | 1.7 | 1.2 |
Physical Analysis | ||||||
Service Temp. ˚C | 1550 | 1600 | 1600 | 1700 | 1700 | 1800 |
Bulk Density gms/cc | 2.30 | 2.60 | 2.70 | 2.90 | 3.00 | 3.10 |
Water required for casting % | 4.8 - 5.5 | 4.7 – 5.4 | 4.7 – 5.4 | 4.2 – 5.0 | 4.2 – 5.0 | 4.0 – 4.8 |
Grain Size, mm | 6 | 6 | 6 | 6 | 6 | 6 |
Cold Crushing | ||||||
Strength Kgs/cm2 | ||||||
At 110 ˚C/24 hrs. | 700 | 750 | 750 | 800 | 950 | 1000 |
At 800 ˚C/3 hrs. | 800 | 800 | 800 | 900 | 1000 | 1050 |
At 1100 ˚C/3 hrs. | 900 | 900 | 900 | 1000 | 1100 | 1100 |
At 1500 ˚C/3 hrs. | 1000 | 1000 | 1000 | 1200 | 1200 | 1250 |
C,% DLC | ||||||
At 800˚C/3 hrs | ± 0.20 | ± 0.2 | ± 0.2 | ± 0.2 | ± 0.20 | ± 0.20 |
At 1100˚C/3 hrs | ± 0.30 | ± 0.30 | ± 0.30 | ± 0.30 | ± 0.30 | ± 0.30 |
at 1500˚C/3 hrs | ± 1.00 | ± 1.00 | ± 0.80 | ± 0.80 | ± 0.80 | ± 0.80 |
Thermal Conductivity | ||||||
Kcal/m/h/˚C | ||||||
At 300 ˚C HF | 0.84 | 0.96 | 1.16 | 1.68 | 2.20 | 2.25 |
At 500 ˚C HF | 1.04 | 1.10 | 1.23 | 1.75 | 2.31 | 2.30 |
At 800 ˚C HF | 1.16 | 1.20 | 1.29 | 1.80 | 2.35 | 2.35 |