Auto Component Sectors

Auto Component Sectors

We have exact and perfect coating solutions for all auto components . All these products have excellent corrosion resistance and durability.



2K POLYURETHANE MONOCOAT PAINT

Specially designed to meet the specific requirement of durable anticorrosive property in single coat system for Steel Structure, large machinery (packaging Industries), Auto Component & Transformers.

PRODUCT SPECIFICATIONS :
  • Excellent adhesion
  • Scratch hardness passes for 2000 gm
  • D.F.T. 60 to 80 microns
  • 500-700 hours Salt Spray by ASTM B-117
  • 240 hours Humidity resistance
  • Good weathering properties
    •

    A) Epoxy High Build Zinc Phosphate Structure Primer :

    This is high performance high build primer specially designed for applying on fully built vehicle structures made of G.I. & Aluminum & is having excellent adhesion, corrosion resistance properties. It also has excellent covering capacity.

    PRODUCT SPECIFICATIONS:
  • Excellent Corrosion Resistance
  • Excellent Adhesion and hardness
  • 300-500 hours salt spray
  • Excellent Flexibility


    • B) Synthetic Quick Drying Structure Primer :

    This is high performance primer specially designed for applying on fully built vehicle structures made Mild Steel is having excellent adhesion, good corrosion resistance properties. It also has faster drying properties.

    PRODUCT SPECIFICATIONS:
  • Faster drying properties
  • Excellent Adhesion and hardness
  • 180 hours salt spray
  • Excellent Flexibility
  • Cost effective as compare to epoxy Structure primer


    • PRODUCT SPECIFICATIONS:

    This paint is specially formulated as a High Build Single coat. It has excellent Adhesion, corrosion resistance properties and chemical resistance properties and it has very good hardness.

    PRODUCT SPECIFICATIONS:
  • Excellent adhesion
  • Scratch hardness passes for 2000 gm
  • D.F.T. 60 to 80 microns
  • 500 hours Salt Spray by ASTM B-117
  • 240 hours Humidity resistance
  • Excellent Chemical Resistance
  • Cost effective in Epoxy Paints


    • TWO PACK WASH PRIMER YELLOW
    Product Description : Barrier Coat Primer
    Recommended use : Galvanized steel surface and Aluminum surface
    Features :
  • Excellent Adhesion Properties on G.I.
  • Recoat ability with any type of Primer
    		•
    Physical Properties : Colour Shade Pale yellow
    D.F.T. 5 to 8 microns
    Theoretical spreading rate 80 to 90 sq. feet @ D.F.T. 05 to 8 μ
    Flash point Base - 23° C ; Hardner - 28° C
    Sp. Gravity Base 1.0 (± 0.05 ) kg per Ltr.
    Hardner 0.90 (± 0.05) kg / Ltr
    Surface Preparation :
  • Surface to be coated should be completely clean, dry and free from contamination.
  • Remove oil & grease with suitable solvent or detergent
  • Remove rust, mill scale and other loose material by wire mesh / abrasive blasting
    		•
    Performance Properties : Excellent Adhesion on Galvanize / Aluminum / plated surface
    Application : Application Conditions Ambient temperature shall be above 10°C and relative humidity shall be below 85%.
    Adequate ventilation shall be provided in confined spaces
    Mixing Stir each component with mechanical stirrer before mixing
    Mixing ratio Base : 1 part, Hardner : 1 part (by volume)
    Application method By air assisted spray gun
    Pot Life Minimum 4 hours at 30°C
    (Pot life may be reduced at higher temperature)
    Drying Time Surface Dry - 03 to 05 minutes
    Touch Dry - 10 to 15 minutes
    Over Coating Minimum - 2 hours maximum - 16 hours
    Shelf Life Base : 6 months; Hardner : 6 months from the date of mfg


    2K POLYURETHANE GLOSSY PAINT
    Product Description : 2K Polyurethane top Coat for Auto Refinishing
    Recommended use : Automobile Products, Bus Body, Farm equipments & commercial vehicles
    Features :
  • Excellent durability
  • Smooth & glossy fin
    		•
    Physical Properties : Colour Shade As per customer requirement
    Volume Solids 48 (± 3 %)
    D.F.T. 30 to 40 microns
    Theoretical Coverage 8 to 9 sq. meter @ D.F.T. 25-30 μ
    Flash point Base - 24° C ; Hardner - 28° C
    Sp. Gravity Base 1.15 (± 0.1) kg / Ltr.
    Hardner 1.05 (± 0.05) kg / ltr
    Surface Preparation :
  • Surface to be coated should be completely clean , dry and free from contamination.
  • Remove oil & grease with suitable solvent or detergent
  • Remove rust, mill scale and other loose material by wire mesh / abrasive blasting
    		•
    Performance Properties : Accelerator Weathering Test : passes for minimum 750 hours Salt Spray resistance – passes 500 hours
    Application : Application Conditions Ambient temperature shall be above 10°C and relative humidity shall be below 85%.
    Adequate ventilation shall be provided in confined spaces
    Mixing Stir each component with mechanical stirrer before mixing
    Mixing ratio Paint : 4 parts, Hardner : 1 part , Thinner : 1 part (by volume)
    Application method By air assisted spray gun
    Pot Life Minimum 5 hours at 30°C
    (Pot life may be reduced at higher temperature)
    Drying Time Surface Dry – 15 to 20 minutes
    Touch Dry – 2 to 3 hours
    Over coating interval Minimum 1 to 2 hours
    Typical undercoat P.U. Primer
    Shelf Life Base : 12 months; Hardner : 6 months from the date of mfg.


    2K POLYUREHTHANE PRIMER SURFACER GREY
    Product Description : 2K Polyurethane Primer
    Recommended use : Automobile Products, Bus Body , Farm equipments & commercial vehicles
    Features :
  • Excellent Adhesion & Flexibility
  • Smooth & eggshell finish
  • Good intercoat adhesion
    		•
    Physical Properties : Colour Shade Grey OR Buff
    Volume Solids 45 (± 3 %)
    D.F.T. 30 to 40 microns
    Theoretical Coverage 8 to 9 sq. meter @ D.F.T. 25-30 μ
    Flash point Base - 24° C ; Hardner - 28° C
    Sp. Gravity Base 1.35 (± 0.1) kg / Ltr.
    Hardner 0.95 (± 0.05) kg / ltr
    Surface Preparation :
  • Surface to be coated should be completely clean , dry and free from contamination.
  • Remove oil & grease with suitable solvent or detergent
  • Remove rust, mill scale and other loose material by wire mesh / abrasive blasting
    		•
    Performance Properties : Salt Spray resistance – passes 500 hours for total system Resistance to moisture – passes for 240 hours
    Application : Application Conditions Ambient temperature shall be above 10°C and relative humidity shall be below 85%.
    Adequate ventilation shall be provided in confined spaces
    Mixing Stir each component with mechanical stirrer before mixing
    Mixing ratio Paint : 4 parts, Hardner : 1 part , Thinner : 1 part (by volume)
    Application method By air assisted spray gun
    Pot Life Minimum 5 hours at 30°C
    (Pot life may be reduced at higher temperature)
    Drying Time Surface Dry – 15 to 20 minutes
    Touch Dry – 1 to 1.5 hours
    Over coating interval Minimum 8 hours
    Typical undercoat P.U. Primer
    Shelf Life Base : 12 months; Hardner : 6 months from the date of mfg.


    HIGH PERFORMANCE STOVING PAINT
    Product Description : Mono coat Stoving Paint
    Recommended use : Auto components , Medical equipments & steel Furniture
    Features :
  • Mono coat system
  • Excellent Adhesion
  • Good flexibility
    		•
    Physical Properties : Colour Shade As per customer's requirement
    Volume Solids 48 (± 3 %)
    D.F.T. 25 to 30 microns
    Theoretical Coverage 8 to 9 sq. meter @ D.F.T. 25 μ
    Flash point 23° C
    Sp. Gravity 1.20 (± 0.1 ) kg per Ltr.
    Surface Preparation :
  • Surface to be coated should be completely clean , dry and free from contamination.
  • Remove oil & grease with suitable solvent or detergent
  • Remove rust, mill scale and other loose material by wire mesh / abrasive blasting
    		•
    Performance Properties : Salt Spray – passes 150 hours for total system Petrol- Diesel resistance - Passes
    Application : Application Conditions Ambient temperature shall be above 10°C and relative humidity shall be below 85%.
    Adequate ventilation shall be provided in confined spaces
    Mixing Stir well with mechanical stirrer before application
    Mixing ratio Paint :2 parts, Thinner : 1 part (by volume)
    Application method By air assisted spray gun/ Electrostatic gun
    Stoving schedule 150° C (± 5° C) for 15 minutes
    Shelf Life 12 months from the date of mfg.
    ONE PACK ZINC RICH GREY PRIMER
    Product Description : Anticorrosive Epoxy one pack primer
    Recommended use : Fabricated Steel Structures, Auto body –Commercial Vehicles & Auto
    parts , Casting Components
    Features :
  • High Performance Corrosion resistance
  • Faster drying properties
  • Excellent Adhesion
    		•
    Physical Properties : Colour Shade Grey/ Red Oxide
    Volume Solids 65 (± 3 %)
    D.F.T. 25 to 30 microns
    Theoretical Coverage 8 to 9 sq. meter @ D.F.T. 25 μ
    Flash point 28° C
    Sp. Gravity Base 1.75 (± 0.1 ) kg per Ltr
    Surface Preparation :
  • Surface to be coated should be completely clean , dry and free from contamination.
  • Remove oil & grease with suitable solvent or detergent
  • Remove rust, mill scale and other loose material by wire mesh / abrasive blasting
    		•
    Performance Properties : Salt Spray – passes 200 hours
    Application : Application Conditions Ambient temperature shall be above 10°C and relative humidity shall be below 85%.
    Adequate ventilation shall be provided in confined spaces
    Mixing Stir well with mechanical stirrer before application
    Mixing ratio Base : 3 parts, Thinner : 1 parts (by volume)
    Application method By air assisted spray gun
    Drying Time Surface Dry – 10 to 15 minutes Touch Dry – 1 to 2 hours
    Over coating interval Minimum 8 hours
    Shelf Life 12 months from the date of mfg.